Direct observation of the leakage current in epitaxial diamond Schottky barrier devices by conductive-probe atomic force microscopy and Raman imaging - CentraleSupélec Access content directly
Journal Articles Journal of Physics D: Applied Physics Year : 2014

Direct observation of the leakage current in epitaxial diamond Schottky barrier devices by conductive-probe atomic force microscopy and Raman imaging

Abstract

The origin of the high leakage current measured in several vertical-type diamond Schottky devices is conjointly investigated by conducting probe atomic force microscopy (CP-AFM) and confocal micro-Raman/Photoluminescence (PL) imaging analysis. Local areas characterized by a strong decrease of the local resistance (5-6 orders of magnitude drop) with respect to their close surrounding have been identified in several different regions of the sample surface. The same local areas, also referenced as electrical hot-spots, reveal a slightly constrained diamond lattice and three dominant Raman bands in the low-wavenumber region (590, 914 and 1040 cm-1). These latter bands are usually assigned to the vibrational modes involving boron impurities and its possible complexes that can electrically act as traps for charge carriers. Local current-voltage measurements performed at the hot-spots point out a trap-filled-limited (TFL) current as the main conduction mechanism favoring the leakage current in the Schottky devices.
Fichier principal
Vignette du fichier
1404.0472.pdf (1.4 Mo) Télécharger le fichier
Origin : Publisher files allowed on an open archive

Dates and versions

hal-01099593 , version 1 (17-02-2024)

Identifiers

Cite

José Alvarez, M. Boutchich, Jean-Paul Kleider, T. Teraji, Y. Koide. Direct observation of the leakage current in epitaxial diamond Schottky barrier devices by conductive-probe atomic force microscopy and Raman imaging. Journal of Physics D: Applied Physics, 2014, 47 (35), pp.355102. ⟨10.1088/0022-3727/47/35/355102⟩. ⟨hal-01099593⟩
55 View
0 Download

Altmetric

Share

Gmail Facebook X LinkedIn More